Hot Rolled Harden Aluminum Round Bar 6061 - T651 with Good Oxidation Resistance Aluminum 6061-T651 or T6 manufacturer from China DongGuan RuiYuan Steel Company

Hot Rolled Harden Aluminum Round Bar 6061 - T651 with Good Oxidation Resistance

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: Aluminum 6061-T651 or T6

Hot Rolled Harden

Hot Rolled Harden Aluminum Round Bar 6061 - T651 with Good Oxidation Resistance

Applications:
Aluminum Round Bar 6061-T651 used in the manufacture of heavy-duty structures requiring good
corrosion resistance, truck and marine components, aircraft gun carriage ,railroad cars, furniture, tank
fittings, general structural and high pressure applications, wire products, and in pipelines.

Description:
1. Aluminum , Grade: 6061, T6 or T651
2. Hot rolled, Temper & Pre-stretching ,T651
3.Production leadtime: 25~45days

4Tensile strength: σb (MPa):≥180

Yield strength :σ0.2 (MPa):≥110

Elongation rate: δ5 (%):≥14

Machinability
Machinability in the harder T 4 and T6 tempers is good. It is notably less easy to machine in the annealed

temper.

Forming
Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are

all readily accomplished using standard methods.

Welding
The alloy has very good welding characteristics and may be welded by all of the common welding

techniques. Gas tungsten arc welding is generally used for thin sections (less than 0.032") and gas metal

arc welding is used for heavier sections. Use alloy 4043 filler wire for best results, although a decrease in T

6 properties will result.

Heat Treatment
Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench.

Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air

cooling.

Forging
The alloy is capable of being hot forged at temperatures in the range of 900 F to 750 F.

Competitive Advantage:

Excellent for processing
High welding characteristic
Good corrosion-resistance
High Toughness
High polishing
Easy for painting
Good Oxidation resistance
Non deformation

Competitive price
Fast production leadtime
All the material are inspected with 3 times to meet the highly standards

Chemical composition:

Si	Mn	Cr	Zn	Mg	Ti	Fe	Cu
0.40~0.8	0.15max	0.04~0.35	0.25	0.8~1.2	0.15	0.7	0.15~0.4

Specifications:

Hot rolled condition	aluminum bar (mm)		Brand
	Dia	Length
	2~200	2500~4500	RuiYuan

Related Search

Hot Rolled Round Bar Hot Rolled Flat Bar Cold Rolled Hot Rolled Steel Hot Rolled Hot Rolled Steel Coil Hot Rolled Steel In Coil More>>

Find more related products in following catalogs on Hisupplier.com

Machinery & Industrial Supplies >> Industrial Supplies Agents