Corrosion Resistance Aluminum Round Bar / Rod 6061 T6

Hot Rolled Aluminium Rod 6061 T6

Chemical composition for  Hot Rolled Aluminium Rod 6061 T6

1. Aluminum , Grade: 6061, T6 or T651

2. Hot rolled, Temper & Pre-stretching ,,T651

3.Production leadtime: 25~45days

4. Tensile strength: σb (MPa):≥180

Yield strength :σ0.2 (MPa):≥110

Elongation rate:  δ5 (%):≥14

Forming

Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.

Machinability

Machinability in the harder T 4 and T6 tempers is good. It is notably less easy to machine in the annealed temper.

Welding

The alloy has very good welding characteristics and may be welded by all of the common welding techniques. Gas tungsten arc welding is generally used for thin sections (less than 0.032") and gas metal arc welding is used for heavier sections. Use alloy 4043 filler wire for best results, although a decrease in T 6 properties will result.

Heat Treatment

Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.

Forging

The alloy is capable of being hot forged at temperatures in the range of 900 F to 750 F.

Specifications for Hot Rolled Aluminium Rod 6061 T6

Competitive Advantage:

• Excellent for processing
• High welding characteristic
• Good corrosion-resistance
•  High Toughness
• High polishing
• Easy for painting
• 